在合金鋁板的整個(gè)生產(chǎn)過程中，不可避免地會(huì)遇到許多產(chǎn)品質(zhì)量問題。一些產(chǎn)品質(zhì)量問題是由于在整個(gè)生產(chǎn)過程中工作人員的粗心大意而引起的，而一些產(chǎn)品質(zhì)量問題是由于在應(yīng)用的中后期階段實(shí)際操作不當(dāng)而引起的。因此，鋁板生產(chǎn)廠家實(shí)際上可以避免鋁板產(chǎn)品質(zhì)量問題的根本原因。
In the whole production process of alloy aluminum plate, many product quality problems are inevitable. Some product quality problems are caused by the carelessness of the staff in the whole production process, while some product quality problems are caused by improper operation in the middle and later stages of application. Therefore, aluminum plate manufacturers can actually avoid the root cause of aluminum plate product quality problems.
在鋁板的生產(chǎn)中，可以避免實(shí)際操作和機(jī)械設(shè)備的使用。鋁板存在許多常見的產(chǎn)品質(zhì)量問題，油漬問題是常見的質(zhì)量損失之一。油漬并不意味著鋁板在生產(chǎn)后會(huì)被污染。只是鋁板冷軋之后，鋁板制造商在鋁頭的表面上放了太多的油，并且除了軋制的油膜外還添加了剩余的油脂。在產(chǎn)品咨詢和批量生產(chǎn)的中后期，您會(huì)發(fā)現(xiàn)這種脂肪在外面肉眼可見。
In the production of aluminum plate, the actual operation and the use of mechanical equipment can be avoided. There are many common product quality problems in aluminum plate, and oil stain is one of the common quality losses. Oil stains do not mean that the aluminum plate will be contaminated after production. But after the cold rolling of aluminum plate, the aluminum plate manufacturer put too much oil on the surface of the aluminum head, and in addition to the rolling oil film, it also added the remaining grease. In the middle and later stage of product consultation and mass production, you will find that the fat is visible to the naked eye.

許多油脂主要散布在擠出機(jī)入口和出口的頂部和底部或輥的頸部。飛濺后，它會(huì)滴在盒子的表面上，然后由于擠出機(jī)測厚儀的漏油而在擠出機(jī)滾筒清潔器中被發(fā)現(xiàn)是異常情況，并且這種油的成分很雜而且很臟。由鋁板制造商生產(chǎn)的鋁板表面上的這種油漬會(huì)嚴(yán)重?fù)p害合金鋁板的外觀。
Many oils are mainly distributed at the top and bottom of the extruder inlet and outlet or at the neck of the roller. After splashing, it will drop on the surface of the box, and then due to the oil leakage of the thickness gauge of the extruder, it is found to be abnormal in the roller cleaner of the extruder, and the composition of the oil is very miscellaneous and dirty. This kind of oil stain on the surface of aluminum plate produced by aluminum plate manufacturer will seriously damage the appearance of alloy aluminum plate.
同時(shí)，當(dāng)每個(gè)人都評(píng)估鋁板的質(zhì)量時(shí)，油性缺 陷的數(shù)量是關(guān)鍵標(biāo)準(zhǔn)之一。一方面，由于鋁板的厚度較薄，在隨后的淬火過程中很容易產(chǎn)生泡沫，并且由于表面上殘留的油太多，因此在鋁的表面會(huì)產(chǎn)生大量的殘留物。鋁板，這也將導(dǎo)致中后期的應(yīng)用性能不是很好。另一方面，如果鋁板的外觀足夠干凈，則可以用作室內(nèi)裝飾和包裝產(chǎn)品的美學(xué)要求，否則不能售賣。
At the same time, when everyone evaluates the quality of aluminum plate, the number of oil defects is one of the key criteria. On the one hand, as the thickness of the aluminum plate is relatively thin, it is easy to produce foam during the subsequent quenching process, and because there is too much oil on the surface, a large amount of residue will be produced on the surface of aluminum. Aluminum plate, which will also lead to the late application performance is not very good. On the other hand, if the appearance of aluminum plate is clean enough, it can be used as the aesthetic requirements of interior decoration and packaging products, otherwise it can not be sold.
應(yīng)該立即將其清理干凈，并出于某種原因進(jìn)行適當(dāng)處理。同時(shí)，我們還應(yīng)清理所生產(chǎn)產(chǎn)品的表面。如果鋁板制造商剛開始時(shí)有不干凈的油漬，則將立即報(bào)銷產(chǎn)品。如果將油性產(chǎn)品放到倉庫或銷售市場中，則事后控制產(chǎn)品質(zhì)量總是比較困難，并且存在許多無法解決的售后服務(wù)問題。鋁板也很容易刮擦。
It should be cleaned up immediately and properly disposed of for some reason. At the same time, we should clean the surface of the products. If the aluminum plate manufacturer has unclean oil stains at the beginning, the product will be reimbursed immediately. If the oil products are put into the warehouse or sales market, it is always difficult to control the product quality afterwards, and there are many unsolvable after-sales service problems. Aluminum is also easy to scratch.
實(shí)際上，有很多原因會(huì)導(dǎo)致鋁板刮擦，刮擦或敲打。這可能是由于輥?zhàn)雍蛯?dǎo)輥表面的劃痕引起的。鋁板上的劃痕通常是凹槽狀的疤 痕，當(dāng)它出現(xiàn)在外部時(shí)有時(shí)會(huì)消失或持續(xù)。
In fact, there are many reasons for aluminum scraping, scraping or knocking. This may be caused by scratches on the surface of rollers and guide rollers. Scratches on aluminum plates are usually grooved scars that sometimes disappear or persist when they appear on the outside.